http://hdl.handle.net/11452/22440| Başlık: | Tensile properties of friction stir welded joints of 2024 aluminum alloys in different heat-treated-state |
| Yazarlar: | Uludağ Üniversitesi/Mühendislik Fakültesi/Makine Mühendisliği Bölümü. Uludağ Üniversitesi/Fen-Edebiyat Fakültesi/Fizik Bölümü. Aydın, Hakan Bayram, Ali Uguz, Agah Akay, Sertan Kemal R-7260-2016 16312009400 7004197848 7004907051 24801954600 |
| Anahtar kelimeler: | Heat treatments Welding Mechanical Mechanical-properties Microstructural evolution Aa2024 Al Visualization Flow Te Materials science Alumina Aluminum Aluminum alloys Friction Heat treatment Stainless steel Tribology Welded steel structures Welding Welds 2024 aluminum alloys Al-alloys Base materials C. Heat treatments D. Welding E. Mechanical Friction stir welded joints Friction stirs Precipitation hardenings Thermo-mechanically affected zones Weld zones |
| Yayın Tarihi: | Haz-2009 |
| Yayıncı: | Elsevier Science |
| Atıf: | Aydın, H. vd. (2009). "Tensile properties of friction stir welded joints of 2024 aluminum alloys in different heat-treated-state". Materials & Design, 30(6), 2211-2221. |
| Özet: | In this study, the different heat-treated-state 2024 Al-alloys were friction stir welded. The tensile properties of the joints have a tendency to increase with the precipitation hardening of the base material. The peak tensile properties have been obtained in the T6 (100 degrees C - 10 h) joint. It is observed that the weld zone is strengthened by the friction stir welding process for the 2024-0 joint. The fracture regions are detected near the nugget for W joint, the interface between the nugget and the thermomechanically affected zone for T4 and T6 joints and base material for O joint. |
| URI: | https://doi.org/10.1016/j.matdes.2008.08.034 https://www.sciencedirect.com/science/article/pii/S026130690800424X http://hdl.handle.net/11452/22440 |
| ISSN: | 0264-1275 |
| Koleksiyonlarda Görünür: | Scopus Web of Science |
Bu öğenin dosyaları:
Bu öğeyle ilişkili dosya bulunmamaktadır.
DSpace'deki bütün öğeler, aksi belirtilmedikçe, tüm hakları saklı tutulmak şartıyla telif hakkı ile korunmaktadır.