Başlık: The effects of silicone and pre-fixation temperature on the elastic properties of cotton/elastane woven fabrics
Yazarlar: Uludağ Üniversitesi/Mühendislik Fakültesi/Tekstil Mühendisliği Bölümü.
Gürarda, Ayça
Meriç, Binnaz
35609709500
14919630800
Anahtar kelimeler: Chemistry
Engineering
Materials science
Cotton
Finishing
Silicone
Composition effects
Cotton yarn
Deformation
Elasticity
Elasticity testing
Silicones
Specimen preparation
Textile finishing
Thermal effects
Washing
Cotton blend
Elasticity
Fixing agent
Temperature effect
Woven fabrics
Elastane
Elastane draw ratio
Fabric growth
Pre-fixation temperature
Warp yarn
Weft yarn
Cotton fabrics
Yayın Tarihi: Eyl-2005
Yayıncı: Amer Assoc Textile Chemists Colorists-AATCC
Atıf: Gürarda, A. ve Meriç, B. (2005). "The effects of silicone and pre-fixation temperature on the elastic properties of cotton/elastane woven fabrics". AATCC Review, 5(9), 53-56.
Özet: This paper presents the effects of silicone and pre-fixation temperature on the elastic properties of cotton/elastane woven fabrics, with nylon/elastane air-covered yarn used as weft yarn and cotton yarn used as warp yarn. Three fabric types with three different elastane weft yarn draw ratios were used as experimental samples. The pre-fixation process was applied to all three fabrics at two different temperatures. After finishing, half of the samples were treated with silicone and the other half were only washed. Fabric stretch and fabric growth after a specified extension was determined as elastic properties for weft stretch woven fabrics. The fabric stretch values were between 14-18% and fabric growth or recovery after a specified extension after 30 min were between 0.7-0.9%.
URI: http://hdl.handle.net/11452/24816
ISSN: 1532-8813
Koleksiyonlarda Görünür:Scopus
Web of Science

Bu öğenin dosyaları:
Bu öğeyle ilişkili dosya bulunmamaktadır.
Tüm Öğe Kaydını Göster İstatistikler


DSpace'deki bütün öğeler, aksi belirtilmedikçe, tüm hakları saklı tutulmak şartıyla telif hakkı ile korunmaktadır.