Başlık: An experimental study of the tensile and tribological behaviors of a dual-phase brass
Yazarlar: Uludağ Üniversitesi/Mühendislik Fakültesi.
Durmaş, Ali
Bayram, Ali
55964532400
7004197848
Anahtar kelimeler: Metallurgy & metallurgical engineering
Alloy
Cooling
Heat treatment
Solid solutions
Tensile strength
Tribology
Bainitic transformation temperature
Brass
Yayın Tarihi: 2002
Yayıncı: Metall-Verlag
Atıf: Durmuş, A. ve Bayram, A. (2002). "An experimental study of the tensile and tribological behaviors of a dual-phase brass". Metall, 57(1-2), 45-49.
Özet: The primary objective of this study has been to investigate the mechanical properties of brass having excellent hot-working properties in single-phase beta that were cooled to below the bainitic transformation temperature. For this reason, a group of specimens of Cu-Zn brass were heated to beta-solid solution region (830 degreesC) and another group samples of Cu-Zn brass were heated to alpha-solid solution region (650 degreesC). These materials were hot-quenched to 250 degreesC and 450 degreesC. The mechanical properties of these materials were determined as a function of heat treatments. There was no improvement observed on the mechanical properties with heat treatments.
URI: http://hdl.handle.net/11452/26032
ISSN: 0026-0746
Koleksiyonlarda Görünür:Scopus
Web of Science

Bu öğenin dosyaları:
Bu öğeyle ilişkili dosya bulunmamaktadır.
Tüm Öğe Kaydını Göster İstatistikler


DSpace'deki bütün öğeler, aksi belirtilmedikçe, tüm hakları saklı tutulmak şartıyla telif hakkı ile korunmaktadır.