http://hdl.handle.net/11452/28323| Başlık: | Investigation of the hot ductility of a high-strength boron steel |
| Yazarlar: | Uludağ Üniversitesi/Mühendislik Fakültesi/Makine Mühendisliği Bölümü. Güler, Hande Ertan, Rukiye Özcan, Reşat 55313485800 35772500300 6701611465 |
| Anahtar kelimeler: | Hot ductility Mechanical properties Al-Si-coated 22MnB5 Dynamic recrystallisation Fractography Tensile deformation behaviors Constitutive model Science & technology - other topics Materials science Metallurgy & metallurgical engineering Aluminum coatings Boron Ductility Fractography Fracture Fracture mechanics High strength steel Mechanical properties Silicon Tensile testing Deformation and fracture Ductility loss Dynamic recrystallisation High-temperature ductility Hot tensile testing Hot-tensile tests Increasing temperatures |
| Yayın Tarihi: | 1-Tem-2014 |
| Yayıncı: | Elsevier |
| Atıf: | Güler, H. vd. (2014). "Investigation of the hot ductility of a high-strength boron steel". Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 608, 90-94. |
| Özet: | In this study, the high-temperature ductility behaviour of an Al-Si-coated 22MnB5 sheet was investigated. The mechanical properties of Al-Si-coated 22MnB5 boron steel were examined via hot tensile tests performed at temperatures ranging from 400 to 900 degrees C at a strain rate of 0.083 s(-1). The deformation and fracture mechanisms under hot tensile testing were considered in relation to the testing data and to the fracture-surface observations performed via SEM. The hot ductility of the tested boron steel was observed as a function of increasing temperature and the Al-Si-coated 22MnB5 boron steel exhibited a ductility loss at 700 degrees. |
| URI: | https://doi.org/10.1016/j.msea.2014.04.053 https://www.sciencedirect.com/science/article/pii/S0921509314005164 http://hdl.handle.net/11452/28323 |
| ISSN: | 0921-5093 1873-4936 |
| Koleksiyonlarda Görünür: | Scopus Web of Science |
Bu öğenin dosyaları:
Bu öğeyle ilişkili dosya bulunmamaktadır.
DSpace'deki bütün öğeler, aksi belirtilmedikçe, tüm hakları saklı tutulmak şartıyla telif hakkı ile korunmaktadır.