Başlık: Assessment of color strength and color difference values of polyester fabrics containing continuous weft yarns after abrasion
Yazarlar: Uludağ Üniversitesi/Mühendislik Fakültesi/Tekstil Mühendisliği Bölümü
0000-0002-2655-2773
Akgün, Mine
Becerir, Behçet
Alpay, Halil Rıfat
AAG-9756-2021
AAH-1445-2021
9839293900
9839809500
9841273700
Anahtar kelimeler: Abrasion
Color
Color strength
Disperse dyes
Polyester
Materials science
Polymer science
Wool/polyester blended fabrics
Varying structural parameters
Single-fiber transfer
Ring spun yarns
Cotton fabrics
Open-end
Performance
Reflectance
Resistance
Wool
Yayın Tarihi: 22-Ağu-2007
Yayıncı: Korean Fiber Society
Atıf: Akgün, M. vd. (2007). "Assessment of color strength and color difference values of polyester fabrics containing continuous weft yarns after abrasion". Fibers and Polymers, 8(5), 495-500.
Özet: This paper assesses the color difference and color strength values (K/S) obtained for eight disperse-dyed polyester fabric samples with different fabric construction parameters (weft yam type, weft yam count, weft density and fabric weave) after four sets of abrasion cycles. Warp yarn type and count, warp density, and warp yam twist are the same for all fabrics. Fabric samples are dyed in a commercial red disperse dye (C.I. Disperse Red 74:1) and four different abrasion cycles (2500, 5000, 7500, 10000) are used. The KISS values of the abraided fabrics and color difference values between the control fabric (dyed but not abraided) and abraded fabrics are calculated. The main differences in the KISS and color difference values are observed between 0-2500 abrasion cycles. The high tenacity of the polyester fibers and continuous polyester yams causes some fuzz but no pilling formation on the fabric surface that lead to increased K/S values and color differences. Fiber dullness, yam thickness, yam density and fabric weave are concluded to have different effects on the appearance after abrasion.
URI: https://doi.org/10.1007/BF02875871
https://link.springer.com/article/10.1007%2FBF02875871
http://hdl.handle.net/11452/29269
ISSN: 1229-9197
Koleksiyonlarda Görünür:Scopus
Web of Science

Bu öğenin dosyaları:
Bu öğeyle ilişkili dosya bulunmamaktadır.


DSpace'deki bütün öğeler, aksi belirtilmedikçe, tüm hakları saklı tutulmak şartıyla telif hakkı ile korunmaktadır.