http://hdl.handle.net/11452/32617| Başlık: | Glass forming ability and magnetic properties of Fe36Ni36B19.2Si4.8Nb4−xMx (M = Cu, Zr, Ti, Y, Pt) bulk glassy alloys fabricated by suction casting |
| Yazarlar: | Duman, Nagehan Akdeniz, M. Vedat Uludağ Üniversitesi/Fen-Edebiyat Fakültesi/Fizik Anabilim Dalı. 0000-0002-8871-2357 Kırımlı, Handan Engin Şarlar, Kağan Konuk, Oğuz A. Küçük, İlker Semih AAI-6732-2021 B-8159-2016 24460574700 55550817200 57142470600 6602910810 |
| Anahtar kelimeler: | Physics Bulk metallic glasses (BMGs) Suction casting Magnetic materials Glass forming ability Superhigh strength Differential scanning calorimetry Fabrication Glass Magnetic materials Magnetic properties Metallic glass Platinum alloys Saturation magnetization Silicon Supercooling Titanium alloys As-cast Bulk glassy alloy Bulk metallic glass Glass forming ability Nb addition Suction casting Supercooled liquid region Casting |
| Yayın Tarihi: | May-2013 |
| Yayıncı: | Springer |
| Atıf: | Kırımlı, H. E. vd. (2013). “Glass forming ability and magnetic properties of Fe36Ni36B19.2Si4.8Nb4−xMx (M = Cu, Zr, Ti, Y, Pt) bulk glassy alloys fabricated by suction casting”. Journal of Superconductivity and Novel Magnetism, 26(5), Special Issue, 1683-1685. |
| Özet: | In this study, the effects of Cu, Zr, Ti, Y, Pt substitution for Nb additions on the stability and magnetic properties of Fe-Ni-based bulk metallic glass (BMG) alloys fabricated by the suction casting method are investigated. The saturation magnetization (J(s)) and coercivity (H-c) for as-cast Fe36Ni36B19.2Si4.8Nb4-xMx (M = Cu, Ti) BMG alloys were in the range of 0.51 T-0.55 T and 76-779 A/m, respectively. Differential scanning calorimetry curves show that the Fe36Ni36B19.2Si4.8Nb4-xMx (M = Cu, Ti) bulk metallic glasses have a supercooled liquid region for Cu at 44 K and for Ti at 39 K. |
| URI: | https://doi.org/10.1007/s10948-012-1998-y http://hdl.handle.net/11452/32617 |
| ISSN: | 1557-1939 1557-1947 |
| Koleksiyonlarda Görünür: | Scopus Web of Science |
Bu öğenin dosyaları:
Bu öğeyle ilişkili dosya bulunmamaktadır.
DSpace'deki bütün öğeler, aksi belirtilmedikçe, tüm hakları saklı tutulmak şartıyla telif hakkı ile korunmaktadır.