Başlık: Surface roughness properties of wool woven fabrics after abrasion
Yazarlar: Uludağ Üniversitesi/Mühendislik Fakültesi/Tekstil Mühendisliği Bölümü.
Akgün, Mine
AAG-9756-2021
9839293900
Anahtar kelimeler: Materials science
Surface roughness
Abrasion
Wool woven fabric
Constructional parameters
Color-difference values
Polyester fabrics
Cotton fabrics
Wrinkle recovery
Image-analysis
Seam pucker
Weft yarns
Reflectance
Parameters
Strength
Abrasion
Fabrics
Tribology
Weaving
Wool
Yarn
Constructional parameters
Contact areas
Fabric structures
Weave patterns
Wool fabric
Woven fabrics
Woven wool fabrics
Yarn density
Surface roughness
Yayın Tarihi: 9-Ağu-2015
Yayıncı: Taylor & Francis
Atıf: Akgün, M. (2016). "Surface roughness properties of wool woven fabrics after abrasion". Journal of the Textile Institute, 107(8), 1056-1067.
Özet: Effects of abrasion on surface roughness properties together with appearance of woven wool fabrics have been investigated. The effects of weft yarn count, weft yarn density, and weave pattern on fabric surface roughness after abrasion were researched. Surface roughness values of control fabric (not abraded) and abraded fabrics after four different abrasion cycles were discussed according to different fabric constructional parameters. It was observed that the greatest decreases in surface roughness values after abrasion were observed in loose fabric structures which had the highest initial fabric surface roughness values (coarse yarn, low yarn density, and low yarn intersection). The results showed that change of roughness properties of wool fabric surfaces after abrasion depends on the initial surface roughness values and on the amount of contact area of fabrics based on the fabric constructional parameters.
URI: https://doi.org/10.1080/00405000.2015.1083352
https://www.tandfonline.com/doi/full/10.1080/00405000.2015.1083352
http://hdl.handle.net/11452/33823
ISSN: 0040-5000
1754-2340
Koleksiyonlarda Görünür:Scopus
Web of Science

Bu öğenin dosyaları:
Bu öğeyle ilişkili dosya bulunmamaktadır.


DSpace'deki bütün öğeler, aksi belirtilmedikçe, tüm hakları saklı tutulmak şartıyla telif hakkı ile korunmaktadır.